Technical Specifications

Fibre : 100% BCF Duralox Olefin
Construction : Loop Pile Graphic
Machine Gauge : 1/10″
Tuft Density : -+158 OOO /m2
Pile Thickness : 4-5 mm
Total Thickness : ±6.5 mm
Pile Gross Weight : ca. 20 oz/sqyd
Total Weight : ca. 43 oz/sqyd
Backing : Action Back
Roll Width : 3.66 meter (12′)
Stitches/10CM : 40
Light Fastness : 5-6 (AAPCC 16E)
Flammability : 8 passes (ASTM D-2859-96 & CPSC FF-170)
Suitability : Domestic/Commercial
Design Repeat : 5 cm X 5 cm
• Slight color variations may occur from dye lot to dye lot.

Tokyo samples

Rossini

Rossini

Technical Specifications

Fibre: 100% Coiler Heatset Duralox Olefin
Dye Method : Solution Dyed
Denier: 1450 x 2/ Denier
Construction : Level Cut and Loop (LCL)
Machine Gauge: 1/10″
Tuft Density: 154050/m2
Pile Thickness : 7-8 mm
Total Thickness : 10-11 mm
Pile Gross Weight : ca. 36 Oz/sqyd
Backing : Action Back
Roll Width : 3.66 meter (12)
Static Propensity : Under 3 kV
Smoke Density : Less than
Design Repeat : 8cm (3″) x 8cm (3″)

Rossini samples

New Royal Majestic

New Royal Majestic

Technical Specifications

Fibre 100% Polyamide (Nylon) IMPREL Heatset
ConsttÜCiion : Tufted
Machin Gauge : 1/8″ Plain Saxony
Tuft Density : -+ 186 000 /m2
Pile Thickness mm
Total Thickness mm
Pile Gross Weight : 2400 gms/sq.m (ca.70 oz/sqyd)
Total Weight : 3425 gms/sq.m ca.100 oz/sqyd)
Backing Action Back
Rbil Width : 4
Installation Method : Stretching